BORIDING OF TITANIUM GR2 AND GR5 ALLOYS

Creative Commons License

Ertürk L., Selçuk B.

The International Conference on Material Science and Technology (IMSTEC) 2019, Ankara, Türkiye, 18 - 20 Ekim 2019, ss.46-51

  • Yayın Türü: Bildiri / Tam Metin Bildiri
  • Basıldığı Şehir: Ankara
  • Basıldığı Ülke: Türkiye
  • Sayfa Sayıları: ss.46-51
  • Sivas Cumhuriyet Üniversitesi Adresli: Evet

Özet

Titanium and alloys are used in many fields due to their superior properties such as lightness and high strength. Pack boriding technique to Gr2 and Gr5 samples was carried out at various temperature ranging from 950 to 1050 °C for 6 h, using 85% B4C and 15% Na2CO3 as boriding media. It was determined that borided layers were composed of TiB2 and TiB by means of XRD analysis. The microstructure and elemental analysis of layer on samples were examined by SEM. It found that the thickness of borided layers increased parabolically with increasing boriding temperature. It was seen that diffusion of the boron and microhardness of borided layers went up with rising boriding temperature.