Study on mechanical properties and microstructure for three compounds of Al-Sn-Mg ternary alloys

Alper Billur C., Saatçi B.

PHILOSOPHICAL MAGAZINE, cilt.101, sa.23, ss.2502-2513, 2021 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 101 Sayı: 23
  • Basım Tarihi: 2021
  • Doi Numarası: 10.1080/14786435.2021.1974597
  • Dergi Adı: PHILOSOPHICAL MAGAZINE
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, Academic Search Premier, PASCAL, Aerospace Database, Chemical Abstracts Core, Communication Abstracts, Compendex, INSPEC, Metadex, Civil Engineering Abstracts
  • Sayfa Sayıları: ss.2502-2513
  • Anahtar Kelimeler: Ternary alloys, microstructure, mechanical properties, intermetallic phase, Al-Sn-Mg alloys, extrusion processes, ALUMINUM-ALLOYS, MAGNESIUM
  • Sivas Cumhuriyet Üniversitesi Adresli: Evet

Özet

In the present study, the microstructure and mechanical properties of Al-Sn-Mg ternary alloy were investigated depending on the composition. When the microstructures of the compositions of the alloy are examined, it was observed that Mg2Sn, Mg3Sn1,67 intermetallic phases were formed at the grain boundaries. However, the grain size of each phase changed depending on the composition. It has been observed that such changes in the microstructure affect the mechanical properties of the material. The 94 at. % Al-2.5 at. % Sn-3.5at. % Mg has been found to have the most suitable material properties in terms of ductility and strength. The hardness of [96.5-x] at. % Al-[x] at. % Sn-3.5 at. % Mg (x = 2.5, 8.5 (eutectic composition), 14.5) compounds was measured 52 HV (0.1), 47 HV (0.1), 40 HV (0.1) for bulk samples and 72 HV (0.1), 56 HV0.1, 51 HV (0.1) for rod-shaped samples, respectively.