The Effect of Surface Treatments on Tensile Bond Strength between a Silicone Soft Liner and a Heat-Cured Denture Base Resin
JOURNAL OF ADHESION, cilt.87, sa.9, ss.951-965, 2011 (SCI-Expanded)
- Yayın Türü: Makale / Tam Makale
- Cilt numarası: 87 Sayı: 9
- Basım Tarihi: 2011
- Doi Numarası: 10.1080/00218464.2011.601241
- Dergi Adı: JOURNAL OF ADHESION
- Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
- Sayfa Sayıları: ss.951-965
- Anahtar Kelimeler: Lasing, PMMA, Sandblasting, Silicone soft liner, Tensile bonding, Thermocycling, RESILIENT LINING MATERIALS, ELECTRON-BEAM IRRADIATION, RUPTURE PROPERTIES, MALEIC-ANHYDRIDE, WATER SORPTION, ACRYLIC RESIN, SOLUBILITY
- Sivas Cumhuriyet Üniversitesi Adresli: Evet
Özet
This study evaluated tensile bond strength of a denture soft lining material to a poly (methylmethacrylate) (PMMA) denture base resin subjected to different surface treatment modalities and thermocycling. The materials tested were a silicone-based liner, Molloplast B (R), and a heat-cured denture base resin, Meliodent (TM). The denture soft lining material was packed against cured PMMA base resin, which was smoothed; sandblasted with 250-mu m Al2O3 particles; or lased with a KTP laser; or against uncured PMMA dough (n = 10). In each group, five specimens were thermocycled in a water bath (5-55 degrees C; 3000 cycles) before testing, whereas the other five were directly tested after 24 h. A tensile test was performed using a universal testing machine. Data showed that different treatment modalities of resin surfaces affected adhesion between these two materials and the highest bond values were recorded for cured/smoothed samples under each condition tested. Thermocycling of specimens had no significant reducing effect on measured bond strength values.