The Effect of Ball Milling Speed on the Penetration of Cr And Zr into Cu for Production of Cu1CrZr Alloy Powder
International Scientific Journal Machines. Technologies. Materials., cilt.13, sa.8, ss.362-366, 2019 (Hakemli Dergi)
- Yayın Türü: Makale / Tam Makale
- Cilt numarası: 13 Sayı: 8
- Basım Tarihi: 2019
- Dergi Adı: International Scientific Journal Machines. Technologies. Materials.
- Derginin Tarandığı İndeksler: Other Indexes
- Sayfa Sayıları: ss.362-366
- Açık Arşiv Koleksiyonu: AVESİS Açık Erişim Koleksiyonu
- Sivas Cumhuriyet Üniversitesi Adresli: Evet
Özet
Abstract: The copper alloys are preferred for their superior mechanical properties combined with high electrical conductivity for contact material applications. These properties should be a very good combination of high mechanical strength and enough electrical conduction properties as well as high thermal conductivity. To establish the electrical and thermal conductivity, the low resistive materials such as copper and their alloys to be chosen is a must. Copper can be alloyed with Cr and Zr in very low amounts down to 1 wt% and 0.15 wt%, respectively. These amounts can be found from phase diagrams of interest. The planetary ball milling was chosen as being a unique technique for powder processing to obtain mechanochemical activation and mixing of powders prior to sintering. The ball milling jar was ZrO2 and ball to powder ratio was varied as 1:1, 5:1, and 10:1. The ball milling rotation was ranged from 400 and 500 rpm for different durations to be investigated. The SEM photos showed the Cr and Zr penetration onto Cu powders transformed to flakes of different sizes. The elemental composition maps showed the better and finer distribution of alloying elements at 500 rpm than 400 rpm.
KEYWORDS: CuCr1Zr ALLOY, BALL MILLING, PENETRATION INTO Cu.