Evaluation of a self-adhering flowable composite in terms of micro-shear bond strength and microleakage

Bektas O. O., EREN D., Akin E. G., AKIN H.

ACTA ODONTOLOGICA SCANDINAVICA, cilt.71, ss.541-546, 2013 (SCI-Expanded) identifier identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 71
  • Basım Tarihi: 2013
  • Doi Numarası: 10.3109/00016357.2012.696697
  • Dergi Adı: ACTA ODONTOLOGICA SCANDINAVICA
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.541-546
  • Sivas Cumhuriyet Üniversitesi Adresli: Evet

Özet

Purpose. The objective of this study was to evaluate dentin bond strength and microleakage of a self-adhering flowable resin with or without adhesive resin. Materials and methods. Dentin pieces were randomly assigned to three groups (n = 10): Group OR (Optibond+Revolution Formula 2 Flow); Group VF (Vertise Flow); and Group OVF (Optibond+Vertise Flow). Then specimens were stressed in shear at a cross-head speed of 1 mm/min until the bond failed. Moreover, microleakage was determined by restoring Class V cavities. A statistical analyses was carried out using Mann-Whitney U and Kruskal-Wallis tests (p < 0.05). Results. Group OVF specimens produced the highest mean shear bond strength. In addition, the results showed that the marginal seal in group VF was similar to that in group OR. Conclusion. Self-adhering flowable composite resin combined with adhesive resin provided stronger dentin bond strength and a better marginal seal than when it was used individually. VF is a useful material with an acceptable bond strength and marginal seal.